Case Hardening Steel

Product Details:

Case Hardening EN353 steel bar, EN353 Alloy Steel Bars/ EN353 Round Bars / EN353 Flat Bars.

EN 353 steel has carbon content material of 0.17 % & probably the most usual form of steel, because the carbon content material raises, the material becomes tougher & harder. It's observed that the hardness & wear resistance of the EN 353 steels elevated after the warmness therapy & the micro structure is exchange from ferrite to marten website.
This grade is in general used for a lot of automobiles functions comparable to heavy duty tools, shaft, pinion, cam shafts and gudgeoned pins.

EN353 Alloy Steel Bars/ EN353 Round Bars / EN353 Flat Bars can be avail as rolled, forged in annealed condition with black or bright (peeled or proof machined) finish.

Size Specifications: Can offer EN353 Alloy Steel Bars/ EN353 Round Bars / EN353 Flat Bars in size range of 25mm upto 250mm in diameter.

Chemical composition of EN353 Alloy Steel Bars/ EN353 Round Bars / EN353 Flat Bars:

Element: Percentage

Carbon, C: 0.14-0.20

Silicon, Si: 0.10-0.40

Manganese, Mn: 0.60-0.90

Chromium, Cr: 0.80-1.20

Molybdenum, Mo: 0.10-0.20

Nickel, Ni: 1.20-1.70

Additional Information:

• Delivery Time: 1 day

Product Details:

We are the supplier and trader of wide range of 20MnCr5 Steel Round Bars. We use supreme quality of raw materials to make these products along with the most advanced technology. These are procured from reputed vendors after thorough testing and inspection by our team of procuring agents. These are highly recognized in gears, gear shafts and many other applications.

Chemical Composition:

Additional Information:

• Delivery Time: 1 Day

Product Details:

the low-carbon iron within a substance high in carbon, then heating this pack to encourage carbon migration into the surface of the iron. 

Product Details:

16MnCr5 grade steel is a case hardening steel used extensively for both carburising and carbonitriding, demonstrating reasonably high hardenability and excellent forgeability.

This grade also has excellent weldability, however care should be taken to avoid weld cracking.

Machinability is approximately 80% of that of mild steel

Additional Information:

• Delivery Time: 1 day

Product Details:

We are the supplier and trader of wide range of 20MnCr5 Steel Round Bars. We use supreme quality of raw materials to make these products along with the most advanced technology. These are procured from reputed vendors after thorough testing and inspection by our team of procuring agents. These are highly recognized in gears, gear shafts and many other applications.

Chemical Composition:

Product Details:

16MnCr5 steel are alloyed case hardening engineering steels for parts which require core tensile strength of 800 – 1100 N/mm² and good wearing resistance. It is an engineering material typically used to manufacture piston bolts, camshafts, levers and other vehicle and mechanical engineering components.
CHEMICAL COMPOSITION % OF GRADE 16MNCR5  STEEL (1.7131): EN 10084-2008

Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser, other than for the purpose of finishing the heat.

• C
• 0.14 – 0.19

• Si
• max 0.4

• Mn
• 1 – 1.3

• P
• max 0.025

• S
• max 0.035

• Cr
• 0.8 – 1.1                                                    

Soft Annealing
Heat to 650-700^oC, cool slowly.

Intermediate Annealing
Temperature: 650-680^oC.

Normalizing
Temperature: 850-880^oC.

Carburizing
Temperature: 880-980^oC.

Case Hardening
Temperature: 780-820^oC.

Core Hardening
Harden from a temperature of 860-980^oC followed by water, oil or thermal bath quenching.

Tempering
Tempering temperature: 150-200^oC.

Forging
Hot forming temperature: 1100-850^oC.

Product Details:

Product Description : EN36 is a carburising steel grade with very high surface strength with a soft but strong core. The material retains a remarkable degree of toughness. With high tensile strength, EN36 is used in the production of numerous high strength parts including crankshafts in the automotive and aerospace sector. 

Product Details:

Case Hardening EN353 steel bar, EN353 Alloy Steel Bars/ EN353 Round Bars / EN353 Flat Bars.

EN 353 steel has carbon content material of 0.17 % & probably the most usual form of steel, because the carbon content material raises, the material becomes tougher & harder. It's observed that the hardness & wear resistance of the EN 353 steels elevated after the warmness therapy & the micro structure is exchange from ferrite to marten website.
This grade is in general used for a lot of automobiles functions comparable to heavy duty tools, shaft, pinion, cam shafts and gudgeoned pins.

EN353 Alloy Steel Bars/ EN353 Round Bars / EN353 Flat Bars can be avail as rolled, forged in annealed condition with black or bright (peeled or proof machined) finish.

Size Specifications: Can offer EN353 Alloy Steel Bars/ EN353 Round Bars / EN353 Flat Bars in size range of 25mm upto 250mm in diameter.

Chemical composition of EN353 Alloy Steel Bars/ EN353 Round Bars / EN353 Flat Bars:

Element: Percentage

Carbon, C: 0.14-0.20

Silicon, Si: 0.10-0.40

Manganese, Mn: 0.60-0.90

Chromium, Cr: 0.80-1.20

Molybdenum, Mo: 0.10-0.20

Nickel, Ni: 1.20-1.70

Additional Information:

• Item Code: EN353